Cast iron is a class of iron – carbon alloys with a carbon content of more than 2% and silicon content around 1–3%. [ 1] Its usefulness derives from its relatively low melting temperature. The alloying elements determine the form in which its carbon appears: white cast iron has its carbon combined into an iron carbide named cementite, which ...
In heat transfer, the thermal conductivity of a substance, k, is an intensive property that indicates its ability to conduct heat. For most materials, the amount of heat conducted varies (usually non-linearly) with temperature. [ 1] Thermal conductivity is often measured with laser flash analysis. Alternative measurements are also established.
Chvorinov's rule. Chvorinov's rule is a physical relationship that relates the solidification time for a simple casting to the volume and surface area of the casting. It was first expressed by Czech engineer Nicolas Chvorinov in 1940. [ 1][ 2]
Malleable iron. Wrought iron. Micrograph of grey cast iron. Gray iron, or grey cast iron, is a type of cast iron that has a graphitic microstructure. It is named after the gray color of the fracture it forms, which is due to the presence of graphite. [ 1] It is the most common cast iron and the most widely used cast material based on weight.
Tempering is a heat treatment technique applied to ferrous alloys, such as steel or cast iron, to achieve greater toughness by decreasing the hardness of the alloy. The reduction in hardness is usually accompanied by an increase in ductility, thereby decreasing the brittleness of the metal.
Thermal conductivity and resistivity. The thermal conductivity of a material is a measure of its ability to conduct heat. It is commonly denoted by , , or and is measured in W·m −1 ·K −1 . Heat transfer occurs at a lower rate in materials of low thermal conductivity than in materials of high thermal conductivity.
Malleable iron is cast as white iron, the structure being a metastable carbide in a pearlitic matrix. Through an annealing heat treatment, the brittle structure as first cast is transformed into the malleable form. Carbon agglomerates into small roughly spherical aggregates of graphite, leaving a matrix of ferrite or pearlite according to the ...
Electrical properties. Volume resistivity (ρ) 32.5–39.2 nOhm·m. 6061 aluminium alloy ( Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements. Originally called "Alloy 61S", it was developed in 1935. [ 2]