Cast iron. Cast iron is a class of iron – carbon alloys with a carbon content of more than 2% and silicon content around 1–3%. [ 1] Its usefulness derives from its relatively low melting temperature. The alloying elements determine the form in which its carbon appears: white cast iron has its carbon combined into an iron carbide named ...
Density (at 20° C) 7.874 g/cm 3 ... The broken surface of a white cast iron is full of fine facets of the broken iron carbide, a very pale, silvery, shiny material ...
Malleable iron. Wrought iron. Micrograph of grey cast iron. Gray iron, or grey cast iron, is a type of cast iron that has a graphitic microstructure. It is named after the gray color of the fracture it forms, which is due to the presence of graphite. [ 1] It is the most common cast iron and the most widely used cast material based on weight.
New York: The International Nickel Company, Inc., 1941: 16. — "Values ranging from 21.3 to 21.5 gm/cm 3 at 20 °C have been reported for the density of annealed platinum; the best value being about 21.45 gm/cm 3 at 20 °C." 21.46 g/cm 3 — Rose, T. Kirke. The Precious Metals, Comprising Gold, Silver and Platinum.
Wrought iron. Steel is an alloy of iron and carbon with improved strength and fracture resistance compared to other forms of iron. Because of its high tensile strength and low cost, steel is one of the most commonly manufactured materials in the world. Steel is used in buildings, as concrete reinforcing rods, in bridges, infrastructure, tools ...
Ductile iron. Ductile iron, also known as ductile cast iron, nodular cast iron, spheroidal graphite iron, spheroidal graphite cast iron[ 1] and SG iron, is a type of graphite -rich cast iron discovered in 1943 by Keith Millis. [ 2] While most varieties of cast iron are weak in tension and brittle, ductile iron has much more impact and fatigue ...
Magnox (alloy), whose name is an abbreviation for "magnesium non-oxidizing", is 99% magnesium and 1% aluminium, and is used in the cladding of fuel rods in magnox nuclear power reactors. Magnesium alloys are referred to by short codes (defined in ASTM B275) which denote approximate chemical compositions by weight.
The carbon equivalent is a measure of the tendency of the weld to form martensite on cooling and to suffer brittle fracture. When the carbon equivalent is between 0.40 and 0.60 weld preheat may be necessary. When the carbon equivalent is above 0.60, preheat is necessary, postheat may be necessary. The following carbon equivalent formula is used ...